ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
LNP STAT-KON EX01407C compound is based on Polyetherimide (PEI) resin containing carbon fiber and PTFE. Added features of this grade include: LNP Clean Compounding Technology, Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 273 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
Multiaxial Impact | 3 | J | ISO 6603 |
Instrumented Dart Impact Total Energy, 23°C | 15 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | 16 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 150 | °C | |
Drying Time | 4 - 6 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 360 - 375 | °C | |
Rear - Zone 1 Temperature | 355 - 365 | °C | |
Middle - Zone 2 Temperature | 360 - 370 | °C | |
Front - Zone 3 Temperature | 365 - 375 | °C | |
Nozzle Temperature | 365 - 375 | °C | |
Mold Temperature | 140 - 180 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw speed (Circumferential speed) | 0.2 - 0.3 | m/s | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 5 mm/min | 88 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 11220 | MPa | ASTM D638 |
Flexural Stress, brk, 1.3 mm/min, 50 mm span | 140 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 8950 | MPa | ASTM D790 |
Tensile Stress, break, 5 mm/min | 89 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 10320 | MPa | ISO 527 |
Flexural Stress | 147 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 9640 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.4 | - | ASTM D792 |
Density | 1.399 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.13 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 0.55 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.77 | % | ASTM D955 |
Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 214 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 209 | °C | ASTM D648 |
CTE, -30°C to 30°C, flow | 1.4E-05 | 1/°C | ASTM D696 |
CTE, -30°C to 30°C, xflow | 3.8E-05 | 1/°C | ASTM D696 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 216 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 209 | °C | ISO 75/Af |