LNP™ STAT-KON™ Compound EX12310C

LNP STAT-KON EX12310C compound is based on Polyetherimide (PEI) resin containing 10% carbon fiber. Added features of this grade include: LNP Clean Compounding Technology, Low C18-C40 Hydrocarbons, Electrically Conductive, Dimensional Stability.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Dimensional stability
Electrically Conductive
High stiffness/Strength
High temperature resistance
Low ionics/Outgassing/Liquid particle count
No PFAS intentionally added

Industry

Material previously used in

Electrical
Electronic Components
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Data Management
data storage
hdd component
hard disk drive
hdd spoiler
hdd air diverter
hdd ramp
disk separator
dsp
bits
carrier tape
foup
media
wafer basket
ic chip carrier
low extraction
wafer handling
hard drive
hdd

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	5.08E+05	Ω.cm	ASTM D257
Surface Resistivity	3.97E+05	Ω	ASTM D257

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥0.4	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	32	J/m	ASTM D256
*Charpy Impact, notched, 23°C, 80104mm, Cut*	3	kJ/m²	ISO 179/1eA

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	360 - 400	°C
Rear - Zone 1 Temperature	360 - 380	°C
Middle - Zone 2 Temperature	370 - 390	°C
Front - Zone 3 Temperature	380 - 400	°C
Nozzle Temperature	390 - 400	°C
Mold Temperature	140 - 180	°C
Back Pressure	0.3 - 0.7	MPa
Screw speed (Circumferential speed)	0.2 - 0.3	m/s
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	158	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.4	%	ASTM D638
Tensile Modulus, 5 mm/min	9170	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	224	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	8140	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	156	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.3	%	ISO 527
Tensile Modulus, 1 mm/min	8970	MPa	ISO 527
Flexural Stress, break, 2 mm/min	225	MPa	ISO 178
Flexural Modulus, 2 mm/min	8410	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Water Absorption, (23°C/24hrs)	0.25	%	ASTM D570
Water Absorption, (23°C/Saturated)	1.25	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.2 - 0.4	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.5 - 0.7	%	ASTM D955
Melt Flow Rate, 367°C/6.6 kgf	31	g/10 min	ASTM D1238
Density (Molded)	1.31	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 6.4 mm, unannealed	197	°C	ASTM D648
CTE, 40°C to 120°C, flow	1.56E-05	1/°C	ASTM E831
CTE, 40°C to 120°C, xflow	6.25E-05	1/°C	ASTM E831
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	201	°C	ISO 75/Af
Relative Temp Index, Elec	105	°C	UL 746B
Relative Temp Index, Mech w/impact	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	105	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES