LNP STAT-KON FX98501 compound is based on Polyethylene (PE) resin containing conductive carbon powder and glass fiber. Added features of this grade include: Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+02 - 1.E+05 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 541 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 151 | J/m | ASTM D256 |
| Multiaxial Impact | 4 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 11 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 31 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 230 | °C | |
| Front - Zone 3 Temperature | 220 - 230 | °C | |
| Middle - Zone 2 Temperature | 210 - 220 | °C | |
| Rear - Zone 1 Temperature | 195 - 205 | °C | |
| Mold Temperature | 40 - 55 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 39 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 29 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 5.8 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 8.5 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 3340 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2230 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 36 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 32 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 5.6 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 7.7 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2820 | MPa | ISO 527 |
| Flexural Stress | 45 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2350 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.01 | % | ASTM D570 |
| Density | 1.08 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.02 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 118 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 88 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 9.1E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 1.29E-04 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 114 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 85 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+02 - 1.E+05 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 40 | MPa | ISO 527 |
| Tensile Modulus, 1 mm/min | 2820 | MPa | ISO 527 |
| Flexural Modulus | 2630 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 85 | °C | ISO 75/Af |