ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
LNP STAT-KON IS000XXL compound is based on Nylon 6/12 resin containing stainless steel fiber. Added features of this grade include: Food Contact Compliant, Metal Detectable, Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 486 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 27 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 2 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.12 - 0.2 | % | |
Melt Temperature | 270 - 275 | °C | |
Front - Zone 3 Temperature | 270 - 280 | °C | |
Middle - Zone 2 Temperature | 260 - 270 | °C | |
Rear - Zone 1 Temperature | 255 - 265 | °C | |
Mold Temperature | 65 - 95 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 5 mm/min | 67 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 9.3 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 10.2 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 3040 | MPa | ASTM D638 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2670 | MPa | ASTM D790 |
Tensile Stress, break, 5 mm/min | 66 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 8.5 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 3070 | MPa | ISO 527 |
Flexural Stress | 82 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2430 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.18 | - | ASTM D792 |
Density | 1.18 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.2 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 1 - 3 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 2 - 4 | % | ASTM D955 |
Moisture Absorption (23°C / 50% RH) | 0.29 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 180 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 92 | °C | ASTM D648 |
CTE, -30°C to 30°C, flow | 1.02E-04 | 1/°C | ASTM D696 |
CTE, -30°C to 30°C, xflow | 1.19E-04 | 1/°C | ASTM D696 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 161 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 72 | °C | ISO 75/Af |