LNP STAT-KON JK800 compound is based on Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend containing 8% carbon fiber. Added features of this grade include: Electrically Conductive, Good Hydrolytic Stability, Non-Brominated, Non-Chlorinated Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | 1.E+03 | Ω.cm | ASTM D257 |
| Surface Resistivity | 1.E+06 | Ω | ASTM D257 |
| Static Decay, 5000V to <50V | <0.01 | Seconds | FTMS101B |
| Hot-Wire Ignition (HWI), PLC 0 | ≥1 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1 | mm | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Yellow Card Link 2 | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | ≥1 | mm | UL 94 |
| UL Recognized, 94-5VB Flame Class Rating | ≥1.5 | mm | UL 94 |
| Glow Wire Ignitability Temperature, 1.5 mm | 800 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 1.5 mm | 960 | °C | IEC 60695-2-12 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 347 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 37 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 82 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 21 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 75 - 80 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.04 | % | |
| Melt Temperature | 230 - 275 | °C | |
| Nozzle Temperature | 230 - 275 | °C | |
| Front - Zone 3 Temperature | 225 - 275 | °C | |
| Middle - Zone 2 Temperature | 215 - 260 | °C | |
| Rear - Zone 1 Temperature | 210 - 255 | °C | |
| Mold Temperature | 50 - 70 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 30 - 80 | % | |
| Vent Depth | 0.038 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 96 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 96 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 1.9 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 1.9 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 7580 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 144 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 6200 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 95 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 95 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 145 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 145 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6380 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.25 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.1 - 0.2 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.2 - 0.4 | % | SABIC method |
| Melt Flow Rate, 260°C/2.16 kgf | 17 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 111 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 97 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 92 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 94 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.52E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 6.48E-05 | 1/°C | ASTM E831 |
| CTE, 23°C to 80°C, flow | 2.6E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/120 | 101 | °C | ISO 306 |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.