LNP™ STAT-KON™ Compound KD000

LNP STAT-KON KD000 compound is based on POM (Acetal) copolymer resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Acetal (POM) Copolymer

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
No PFAS intentionally added

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Document Handling
Electronic Components
Fuel Handling
Lawn/Garden
Personal Computing
Vacuum Cleaner
chassis
atm
printer
copier
scanner
optical box
fuel line connector
fuel line clip
filter housing
tank inlet
switch
bezel
household appliance
domestic appliance

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+02 - 1.E+04	Ω	ASTM D257

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	0.7	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	800	J/m	ASTM D4812
Izod Impact, notched, 23°C	35	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	5	J	ASTM D3763
Multiaxial Impact	1	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	37	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Melt Temperature	200 - 215	°C
Front - Zone 3 Temperature	210 - 220	°C
Middle - Zone 2 Temperature	195 - 205	°C
Rear - Zone 1 Temperature	175 - 190	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	58	MPa	ASTM D638
Tensile Stress, break	54	MPa	ASTM D638
Tensile Strain, yield	3.6	%	ASTM D638
Tensile Strain, break	7.2	%	ASTM D638
Tensile Modulus, 50 mm/min	3500	MPa	ASTM D638
Flexural Stress	95	MPa	ASTM D790
Flexural Modulus	3250	MPa	ASTM D790
Tensile Stress, yield	53	MPa	ISO 527
Tensile Stress, break	47	MPa	ISO 527
Tensile Strain, yield	5	%	ISO 527
Tensile Strain, break	20	%	ISO 527
Tensile Modulus, 1 mm/min	3000	MPa	ISO 527
Flexural Stress	82	MPa	ISO 178
Flexural Modulus	3200	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.45	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.28	%	ASTM D570
Mold shrinkage, flow (mold temp=60°C)	1.2 - 1.3	%	SABIC method
Mold shrinkage, flow (mold temp=100°C)	1.5 - 1.6	%	SABIC method
Mold Shrinkage, flow, 24 hrs	1.5 - 3.5	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1.5 - 3.5	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	1.5 - 3.5	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.5 - 3.5	%	ISO 294
Mold shrinkage, xflow (mold temp=60°C)	0.9 - 1	%	SABIC method
Mold shrinkage, xflow (mold temp=100°C)	1.1 - 1.2	%	SABIC method
Density	1.45	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.33	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	108	°C	ASTM D648
CTE, -40°C to 40°C, flow	1.01E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.01E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.02E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.01E-04	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	105	°C	ISO 75/Af

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+02 - 1.E+04	Ω	ASTM D257

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Yellow Card Link 2	View	-	-
UL Recognized, 94HB Flame Class Rating	0.7	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	800	J/m	ASTM D4812
Izod Impact, notched, 23°C	35	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	5	J	ASTM D3763
Multiaxial Impact	1	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	37	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Melt Temperature	190 - 215	°C
Front - Zone 3 Temperature	200 - 220	°C
Middle - Zone 2 Temperature	190 - 200	°C
Rear - Zone 1 Temperature	180 - 190	°C
Mold Temperature	60 - 110	°C
Back Pressure	0.2 - 0.4	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	58	MPa	ASTM D638
Tensile Stress, break	54	MPa	ASTM D638
Tensile Strain, yield	3.6	%	ASTM D638
Tensile Strain, break	7.2	%	ASTM D638
Tensile Modulus, 50 mm/min	3500	MPa	ASTM D638
Flexural Stress	95	MPa	ASTM D790
Flexural Modulus	3250	MPa	ASTM D790
Tensile Stress, yield	53	MPa	ISO 527
Tensile Stress, break	47	MPa	ISO 527
Tensile Strain, yield	5	%	ISO 527
Tensile Strain, break	20	%	ISO 527
Tensile Modulus, 1 mm/min	3000	MPa	ISO 527
Flexural Stress	82	MPa	ISO 178
Flexural Modulus	3200	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.45	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.28	%	ASTM D570
Mold shrinkage, flow (mold temp=60°C)	1.2 - 1.3	%	SABIC method
Mold shrinkage, flow (mold temp=100°C)	1.5 - 1.6	%	SABIC method
Mold Shrinkage, flow, 24 hrs	1.5 - 3.5	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1.5 - 3.5	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	1.5 - 3.5	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.5 - 3.5	%	ISO 294
Mold shrinkage, xflow (mold temp=60°C)	0.9 - 1	%	SABIC method
Mold shrinkage, xflow (mold temp=100°C)	1.1 - 1.2	%	SABIC method
Density	1.45	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.33	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	108	°C	ASTM D648
CTE, -40°C to 40°C, flow	1.01E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.01E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.02E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.01E-04	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	105	°C	ISO 75/Af

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+02 - 1.E+04	Ω	ASTM D257

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	0.7	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	800	J/m	ASTM D4812
Izod Impact, notched, 23°C	35	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	5	J	ASTM D3763
Multiaxial Impact	1	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	37	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Melt Temperature	190 - 215	°C
Front - Zone 3 Temperature	200 - 220	°C
Middle - Zone 2 Temperature	190 - 200	°C
Rear - Zone 1 Temperature	180 - 190	°C
Mold Temperature	60 - 110	°C
Back Pressure	0.2 - 0.4	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	58	MPa	ASTM D638
Tensile Stress, break	54	MPa	ASTM D638
Tensile Strain, yield	3.6	%	ASTM D638
Tensile Strain, break	7.2	%	ASTM D638
Tensile Modulus, 50 mm/min	3500	MPa	ASTM D638
Flexural Stress	95	MPa	ASTM D790
Flexural Modulus	3250	MPa	ASTM D790
Tensile Stress, yield	53	MPa	ISO 527
Tensile Stress, break	47	MPa	ISO 527
Tensile Strain, yield	5	%	ISO 527
Tensile Strain, break	20	%	ISO 527
Tensile Modulus, 1 mm/min	3000	MPa	ISO 527
Flexural Stress	82	MPa	ISO 178
Flexural Modulus	3200	MPa	ISO 178
Flexural Modulus, 2 mm/min	3200	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.45	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.28	%	ASTM D570
Mold shrinkage, flow (mold temp=60°C)	1.2 - 1.3	%	SABIC method
Mold shrinkage, flow (mold temp=100°C)	1.5 - 1.6	%	SABIC method
Mold Shrinkage, flow, 24 hrs	1.5 - 3.5	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1.5 - 3.5	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	1.5 - 3.5	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.5 - 3.5	%	ISO 294
Mold shrinkage, xflow (mold temp=60°C)	0.9 - 1	%	SABIC method
Mold shrinkage, xflow (mold temp=100°C)	1.1 - 1.2	%	SABIC method
Density	1.45	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.33	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	108	°C	ASTM D648
CTE, -40°C to 40°C, flow	1.01E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.01E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.02E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.01E-04	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	105	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

LNP™ STAT-KON™ Compound KD000

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Related Documents

Technical Data Sheets

Register for High value Multi-Point Data