LNP STAT-KON KEL32 compound is based on Acetal Copolymer (POM) resin containing 10% carbon fiber, 15% PTFE. Added features of this grade include: Electrically Conductive, Internally Lubricated, Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+02 - 1.E+04 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 200 - 215 | °C | |
| Front - Zone 3 Temperature | 210 - 220 | °C | |
| Middle - Zone 2 Temperature | 195 - 205 | °C | |
| Rear - Zone 1 Temperature | 175 - 190 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 51 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8400 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 80 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 62 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 6.4 | % | ISO 178 |
| Flexural Modulus, 2 mm/min | 6000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 0.32 | % | SABIC method |
| Density | 1.51 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/24hrs) | 0.31 | % | ISO 62-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 141 | °C | ISO 75/Af |