LNP STAT-KON KS000MXL compound is based on POM (Acetal) copolymer resin containing stainless steel fiber. Added features of this grade include: Low Extractables, Metal Detectable, Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.93E+12 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 929 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
| Multiaxial Impact | 1 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 5 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 57 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 40 | Hrs | |
| Melt Temperature | 200 - 215 | °C | |
| Front - Zone 3 Temperature | 210 - 220 | °C | |
| Middle - Zone 2 Temperature | 195 - 205 | °C | |
| Rear - Zone 1 Temperature | 175 - 190 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 52 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 51 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 11 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 27 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 3010 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2680 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 52 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 51 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 11 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 26 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2880 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 75 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2590 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.73 | - | ASTM D792 |
| Density | 1.724 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.13 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 2.8 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 2.5 | % | ASTM D955 |
| Moisture Absorption (23°C / 50% RH) | 0.21 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 158 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 104 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 9.9E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 9.8E-05 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 149 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 95 | °C | ISO 75/Af |