LNP™ STAT-KON™ Compound KX02764

LNP STAT-KON KX02764 compound is based on POM (Acetal) copolymer resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Acetal (POM) Copolymer

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
No PFAS intentionally added

Industry

Material previously used in

Automotive Under the Hood
Electronic Components
Material Handling

Applications

Possible usage of material

Fuel Handling
fuel line connector
fuel line clip
filter housing
tank inlet
switch
bezel

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.E+02 - 1.E+06	Ω.cm	ASTM D257
Surface Resistivity	1.E+02 - 1.E+06	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	373	J/m	ASTM D4812
Izod Impact, notched, 23°C	42	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	3	J	ASTM D3763
Multiaxial Impact	7	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	52	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	4	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Melt Temperature	200 - 215	°C
Front - Zone 3 Temperature	210 - 220	°C
Middle - Zone 2 Temperature	195 - 205	°C
Rear - Zone 1 Temperature	175 - 190	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	53	MPa	ASTM D638
Tensile Stress, break	47	MPa	ASTM D638
Tensile Strain, yield	3.8	%	ASTM D638
Tensile Strain, break	10.2	%	ASTM D638
Tensile Modulus, 50 mm/min	3480	MPa	ASTM D638
Flexural Stress	100	MPa	ASTM D790
Flexural Modulus	3010	MPa	ASTM D790
Tensile Stress, yield	53	MPa	ISO 527
Tensile Stress, break	46	MPa	ISO 527
Tensile Strain, yield	4	%	ISO 527
Tensile Strain, break	18.1	%	ISO 527
Tensile Modulus, 1 mm/min	3460	MPa	ISO 527
Flexural Stress	96	MPa	ISO 178
Flexural Modulus	3010	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.443	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.18	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	1.5 - 3.5	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1.5 - 3.5	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	1.5 - 3.5	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.5 - 3.5	%	ISO 294
Density	1.43	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.25	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	106	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	103	°C	ISO 75/Af

Register for High value Multi-Point Data