ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity, ROA | <1E+03 | Ω | IEC 60093 |
Volume Resistivity | <1E+03 | Ω.cm | IEC 60093 |
Surface Resistivity | <1E+03 | Ω | ASTM D257 |
Volume Resistivity | <1E+03 | Ω.cm | ASTM D257 |
LNP STAT-KON MD000EXJ compound is based on Polypropylene resin that has been designed towards injection moulding of electrically conductive thin-walled parts for the medical devices industry. Added features of this grade include: Electrically Conductive, extreme flow, excellent moldability.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity, ROA | <1E+03 | Ω | IEC 60093 |
Volume Resistivity | <1E+03 | Ω.cm | IEC 60093 |
Surface Resistivity | <1E+03 | Ω | ASTM D257 |
Volume Resistivity | <1E+03 | Ω.cm | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume resistivity | <15 | Ω.cm | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched 80*10*4 +23°C | 3 | kJ/m² | ISO 180/1A |
Izod Impact, unnotched 80*10*4 +23°C | 40 | kJ/m² | ISO 180/1U |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 49 | kJ/m² | ISO 179/1eU |
Izod Impact, notched, 23°C | 30 | J/m | ASTM D256 |
Izod Impact, unnotched, 23°C | 660 | J/m | ASTM D4812 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 - 90 | °C | |
Drying Time | 2 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Melt Temperature | 210 - 260 | °C | |
Mold Temperature | 50 - 80 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Modulus, 1 mm/min | 1780 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 25 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 2.5 | % | ISO 527 |
Flexural Modulus, 2 mm/min | 1700 | MPa | ISO 178 |
Flexural Strength, 2 mm/min | 42 | MPa | ISO 178 |
Tensile Modulus, 5 mm/min | 1800 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 25 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 3.2 | % | ASTM D638 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 1600 | MPa | ASTM D790 |
Flexural Strength, 1.3 mm/min, 50 mm span | 45 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.0 | g/cm³ | ISO 1183 |
Mold Shrinkage, flow | 1.0 - 1.5 | % | SABIC method |
Mold Shrinkage, xflow | 1.0 - 1.6 | % | SABIC method |
Melt Volume Rate | |||
– Melt Volume Rate, MVR at 230°C/2.16 kg | 45 | cm³/10 min | ISO 1133 |
– Melt Volume Rate, MVR at 190°C/2.16 kg | 17 | cm³/10 min | ISO 1133 |
Specific Gravity | 1.01 | - | ASTM D792 |
Melt Flow Rate, 190°C/2.16 kgf | 15 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 64 | °C | ISO 75/Af |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 105 | °C | ISO 75/Bf |
HDT, 1.82 MPa, 3.2mm, unannealed | 60 | °C | ASTM D648 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 105 | °C | ASTM D648 |
Vicat Softening Temp, Rate B/50 | 105 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 106 | °C | ISO 306 |
Vicat Softening Temp, Rate B/50 | 105 | °C | ASTM D1525 |
Vicat Softening Temp, Rate B/120 | 106 | °C | ASTM D1525 |
CTE, -40°C to 40°C, flow | 8.8E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 9.4E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, flow | 8.8E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 9.4E-05 | 1/°C | ASTM E831 |