LNP™ STAT-KON™ Compound MD000IS

LNP STAT-KON MD000IS compound is based on Polypropylene (PP) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, High Impact, Heat Stabilized.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polypropylene, Unspecified (PP, Unspecified)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
Heat Stabilized
Impact resistant
No PFAS intentionally added

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Electronic Components
Pharmaceutical Manufacturing

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+01 - 1.E+06	Ω	ASTM D257
Static Decay, 5000V to <50V	<0.01	Seconds	FTMS101B

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1553	J/m	ASTM D4812
Izod Impact, notched, 23°C	833	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	24	J	ASTM D3763
Multiaxial Impact	31	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	112	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	65	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Melt Temperature	225 - 250	°C
Front - Zone 3 Temperature	240 - 250	°C
Middle - Zone 2 Temperature	215 - 225	°C
Rear - Zone 1 Temperature	195 - 205	°C
Mold Temperature	30 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	21	MPa	ASTM D638
Tensile Stress, break	17	MPa	ASTM D638
Tensile Strain, yield	9	%	ASTM D638
Tensile Strain, break	133.8	%	ASTM D638
Tensile Modulus, 50 mm/min	480	MPa	ASTM D638
Flexural Stress	27	MPa	ASTM D790
Flexural Modulus	1130	MPa	ASTM D790
Tensile Stress, yield	18	MPa	ISO 527
Tensile Stress, break	17	MPa	ISO 527
Tensile Modulus, 1 mm/min	1100	MPa	ISO 527
Flexural Stress	27	MPa	ISO 178
Flexural Modulus	1200	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	0.98	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.03	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	1.6 - 1.8	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1.6 - 1.8	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	1.6 - 1.8	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.6 - 1.8	%	ISO 294
Density	0.97	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	81	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	52	°C	ASTM D648
CTE, -40°C to 40°C, flow	1.01E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.19E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.01E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.19E-04	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	56	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES