ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+01 - 1.E+06 | Ω | ASTM D257 |
Static Decay, 5000V to <50V | <0.01 | Seconds | FTMS101B |
LNP STAT-KON MD000ISC compound is based on Polypropylene (PP) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, High Impact, Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+01 - 1.E+06 | Ω | ASTM D257 |
Static Decay, 5000V to <50V | <0.01 | Seconds | FTMS101B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 1553 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 833 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 24 | J | ASTM D3763 |
Multiaxial Impact | 31 | J | ISO 6603 |
Izod Impact, unnotched 80*10*4 +23°C | 112 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 65 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 225 - 250 | °C | |
Front - Zone 3 Temperature | 240 - 250 | °C | |
Middle - Zone 2 Temperature | 215 - 225 | °C | |
Rear - Zone 1 Temperature | 195 - 205 | °C | |
Mold Temperature | 30 - 50 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield | 21 | MPa | ASTM D638 |
Tensile Stress, break | 17 | MPa | ASTM D638 |
Tensile Strain, yield | 9 | % | ASTM D638 |
Tensile Strain, break | 133.8 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 480 | MPa | ASTM D638 |
Flexural Stress | 27 | MPa | ASTM D790 |
Flexural Modulus | 1130 | MPa | ASTM D790 |
Tensile Stress, yield | 18 | MPa | ISO 527 |
Tensile Stress, break | 17 | MPa | ISO 527 |
Tensile Modulus, 1 mm/min | 1100 | MPa | ISO 527 |
Flexural Stress | 27 | MPa | ISO 178 |
Flexural Modulus | 1200 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 0.98 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.03 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 1.6 - 1.8 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 1.6 - 1.8 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 1.6 - 1.8 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 1.6 - 1.8 | % | ISO 294 |
Density | 0.97 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 81 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 52 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 1.01E-04 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 1.19E-04 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 1.01E-04 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 1.19E-04 | 1/°C | ISO 11359-2 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 56 | °C | ISO 75/Af |
Relative Temp Index, Elec | 65 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |