LNP STAT-KON ME003S compound is based on Polypropylene (PP) resin containing 15% carbon fiber. Added features of this grade include: Electrically Conductive, Heat Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+03 - 1.E+06 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 128 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 16 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 14 | J | ASTM D3763 |
| Multiaxial Impact | 3 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 1 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 225 - 250 | °C | |
| Front - Zone 3 Temperature | 240 - 250 | °C | |
| Middle - Zone 2 Temperature | 215 - 225 | °C | |
| Rear - Zone 1 Temperature | 195 - 205 | °C | |
| Mold Temperature | 30 - 50 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 47 | MPa | ASTM D638 |
| Tensile Stress, break | 40 | MPa | ASTM D638 |
| Tensile Strain, yield | 0.7 | % | ASTM D638 |
| Tensile Strain, break | 1.3 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 8960 | MPa | ASTM D638 |
| Flexural Stress | 65 | MPa | ASTM D790 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Tensile Stress, yield | 47 | MPa | ISO 527 |
| Tensile Stress, break | 44 | MPa | ISO 527 |
| Tensile Strain, yield | 0.7 | % | ISO 527 |
| Tensile Strain, break | 1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8590 | MPa | ISO 527 |
| Flexural Stress | 62 | MPa | ISO 178 |
| Flexural Modulus | 7000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 0.99 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.4 - 0.6 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 - 0.7 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.52 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.6 | % | ISO 294 |
| Density | 0.99 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 153 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 133 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.88E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 7.02E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 2.90E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 7.0E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 150 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 131 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+03 - 1.E+06 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 320 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 53 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 225 - 250 | °C | |
| Front - Zone 3 Temperature | 240 - 250 | °C | |
| Middle - Zone 2 Temperature | 215 - 225 | °C | |
| Rear - Zone 1 Temperature | 195 - 205 | °C | |
| Mold Temperature | 30 - 50 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 40 | MPa | ASTM D638 |
| Tensile Strain, break | 3 | % | ASTM D638 |
| Flexural Stress | 65 | MPa | ASTM D790 |
| Flexural Modulus | 5100 | MPa | ASTM D790 |