LNP STAT-KON ME006 compound is based on Polypropylene (PP) resin containing 30% carbon fiber. Added features of this grade include: Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+01 - 1.E+03 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 82 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 41 | J/m | ASTM D256 |
| Multiaxial Impact | 3 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 10 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 4 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 225 - 250 | °C | |
| Front - Zone 3 Temperature | 240 - 250 | °C | |
| Middle - Zone 2 Temperature | 215 - 225 | °C | |
| Rear - Zone 1 Temperature | 195 - 205 | °C | |
| Mold Temperature | 30 - 50 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 58 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 57 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 0.5 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 0.5 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 17340 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 78 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 12300 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 56 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 55 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 0.5 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 0.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 13990 | MPa | ISO 527 |
| Flexural Stress | 58 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 12330 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.03 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.4 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 - 0.9 | % | ASTM D955 |
| Density | 1.06 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.03 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 153 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 132 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 2.3E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 5.9E-05 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 153 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 125 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 213 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 225 - 250 | °C | |
| Front - Zone 3 Temperature | 240 - 250 | °C | |
| Middle - Zone 2 Temperature | 215 - 225 | °C | |
| Rear - Zone 1 Temperature | 195 - 205 | °C | |
| Mold Temperature | 30 - 50 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 59 | MPa | ASTM D638 |
| Tensile Strain, break | 0.5 | % | ASTM D638 |
| Flexural Stress | 85 | MPa | ASTM D790 |
| Flexural Modulus | 11030 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ASTM D792 |