LNP™ STAT-KON™ Compound MX01767C

LNP STAT-KON MX01767C compound is based on Polypropylene (PP) resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, LNP Clean Compounding Technology.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polypropylene, Unspecified (PP, Unspecified)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
Low ionics/Outgassing/Liquid particle count
No PFAS intentionally added

Industry

Material previously used in

Electrical
Electronic Components
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Electronic Material Handling
Industrial Material Handling
Semiconductor
Tray

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+03	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1470	J/m	ASTM D4812
Izod Impact, notched, 23°C	130	J/m	ASTM D256
Multiaxial Impact	32	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	37	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	141	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	9	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Melt Temperature	225 - 250	°C
Front - Zone 3 Temperature	240 - 250	°C
Middle - Zone 2 Temperature	215 - 225	°C
Rear - Zone 1 Temperature	195 - 205	°C
Mold Temperature	30 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	32	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	20	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	7.5	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	25.5	%	ASTM D638
Tensile Modulus, 5 mm/min	1760	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	1490	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	31	MPa	ISO 527
Tensile Stress, break, 5 mm/min	22	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	6.6	%	ISO 527
Tensile Strain, break, 5 mm/min	18	%	ISO 527
Tensile Modulus, 1 mm/min	1570	MPa	ISO 527
Flexural Stress	35	MPa	ISO 178
Flexural Modulus, 2 mm/min	1510	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	0.98	-	ASTM D792
Density	0.98	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.02	%	ASTM D570
Mold Shrinkage, flow	1	%	SABIC method
Mold Shrinkage, xflow	2	%	SABIC method
Moisture Absorption (23°C / 50% RH)	0.01	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	95	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	53	°C	ASTM D648
CTE, -40°C to 40°C, flow	9.2E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	9.5E-05	1/°C	ASTM E831
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	89	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	52	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES