LNP™ STAT-KON™ Compound OE004AE

LNP STAT-KON OE004AE compound is based on Polyphenylene Sulfide (PPS) branched resin containing 20% carbon fiber. Added features of this grade include: Easy Molding, Electrically Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphenylene Sulfide, Branched (PPS, Branched)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Electrically Conductive
Good Processability
High stiffness/Strength

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Electrical Components & Infrastructure

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+02 - 1.E+06	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	254	J/m	ASTM D4812
Izod Impact, notched, 23°C	47	J/m	ASTM D256
*Izod Impact, unnotched 80104 +23°C*	12	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	4	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Melt Temperature	315 - 320	°C
Front - Zone 3 Temperature	330 - 345	°C
Middle - Zone 2 Temperature	320 - 330	°C
Rear - Zone 1 Temperature	305 - 315	°C
Mold Temperature	140 - 165	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	163	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	163	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	0.8	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	0.8	%	ASTM D638
Tensile Modulus, 50 mm/min	27160	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	215	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	15710	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	146	MPa	ISO 527
Tensile Stress, break, 5 mm/min	146	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	0.8	%	ISO 527
Tensile Strain, break, 5 mm/min	0.8	%	ISO 527
Tensile Modulus, 1 mm/min	19120	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	208	MPa	ISO 178
Flexural Modulus, 2 mm/min	16050	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.42	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	0.1 - 0.3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.5 - 0.7	%	ASTM D955
Density	1.42	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	279	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	263	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	262	°C	ISO 75/Af

CAE Cards

Please login to view graphs, download multi-point data or literature

Register for High value Multi-Point Data