LNP™ STAT-KON™ Compound PFG03EL

LNP STAT-KON PFG03EL compound is based on Nylon 6 resin containing glass fiber and proprietary thermal filler. Added feature of this grade include: Electrically Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 6 (Nylon 6)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Europe

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Conductive
Electrically Conductive
Food Contact Acceptable
No PFAS intentionally added

Industry

Material previously used in

Food & Beverage

Applications

Possible usage of material

Air Filtration
Building Element
Conveyor
Electrical Components & Infrastructure
Food Transportation
Industrial Material Handling
Infrastructure

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1E+04 - 1E+06	Ω	ANSI/ESD STM11.11
Surface Resistivity	1E+04 - 1E+06	Ω	ASTM D257
Volume Resistivity	1E+01 - 1E+03	Ω.cm	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	15	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Maximum Moisture Content	0.15 - 0.25	%
Drying Temperature	80 - 90	°C
Drying Time	4 - 6	Hrs
Melt Temperature	265 - 295	°C
Nozzle Temperature	260 - 290	°C
Front - Zone 3 Temperature	265 - 295	°C
Middle - Zone 2 Temperature	255 - 285	°C
Rear - Zone 1 Temperature	245 - 275	°C
Mold Temperature	80 - 100	°C
Back Pressure	0.2 - 0.3	MPa
Screw speed (Circumferential speed)	0.15 - 0.25	m/s

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	100	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.3	%	ISO 527
Tensile Modulus, 1 mm/min	13000	MPa	ISO 527
Flexural Stress, break, 2 mm/min	140	MPa	ISO 178
Flexural Modulus, 2 mm/min	12300	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.57	g/cm³	ISO 1183
Mold Shrinkage, flow	0.3 - 0.8	%	SABIC method
Mold Shrinkage, xflow	0.4 - 0.9	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	210	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	205	°C	ISO 75/Af

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity
– Volume Resistivity	-	Ω.cm	ANSI/ESD STM11.11
– Volume Resistivity	-	Ω.cm	ASTM D257
Surface Resistivity	1E+04 - 1E+06	Ω	ANSI/ESD STM11.11
Surface Resistivity	1E+04 - 1E+06	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	15	kJ/m²	ISO 180/1U
Izod Impact, notched, 23°C	50	J/m	ASTM D256
Izod Impact, unnotched, 23°C	210	J/m	ASTM D4812
Charpy
– Charpy 23°C, V-notch Edgew 80104 sp=62mm	10	kJ/m²	ISO 179/1eA
– Charpy 23°C, Unnotch Edgew 80104 sp=62mm	15	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Maximum Moisture Content	0.15 - 0.25	%
Drying Temperature	80 - 90	°C
Drying Time	4 - 6	Hrs
Melt Temperature	265 - 295	°C
Nozzle Temperature	260 - 290	°C
Front - Zone 3 Temperature	265 - 295	°C
Middle - Zone 2 Temperature	255 - 285	°C
Rear - Zone 1 Temperature	245 - 275	°C
Mold Temperature	80 - 100	°C
Back Pressure	0.2 - 0.3	MPa
Screw speed (Circumferential speed)	0.15 - 0.25	m/s

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	13000	MPa	ISO 527
Tensile Stress, break, 5 mm/min	100	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.3	%	ISO 527
Flexural Modulus, 2 mm/min	12250	MPa	ISO 178
Flexural Stress, break, 2 mm/min	140	MPa	ISO 178
Tensile Modulus, 5 mm/min	13000	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	80	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	1.1	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	12500	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	150	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.57	g/cm³	ISO 1183
Moisture Absorption, (23°C/50% RH/24hrs)	0.05	%	ISO 62-4
Moisture Absorption, (23°C/50% RH/Equilibrium)	0.1	%	ISO 62-4
Water Absorption, (23°C/saturated)	0.4	%	ISO 62-1
Water Absorption, (23°C/24hrs)	2.1	%	ISO 62-1
Mold Shrinkage, flow	0.2 - 0.7	%	SABIC method
Mold Shrinkage, xflow	0.4 - 0.9	%	SABIC method
Specific Gravity	1.57	-	ASTM D792
Water Absorption, (23°C/Saturated)	0.4	%	ASTM D570
Water Absorption, (23°C/24hrs)	2.1	%	ASTM D570

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	208	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	215	°C	ISO 75/Bf
HDT, 1.82 MPa, 3.2mm, unannealed	210	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	219	°C	ASTM D648
Vicat Softening Temp, Rate B/50	212	°C	ISO 306
Vicat Softening Temp, Rate B/120	209	°C	ISO 306
Vicat Softening Temp, Rate B/50	212	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	209	°C	ASTM D1525
CTE, -40°C to 40°C, flow	1.8E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	4.5E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, flow	1.8E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	4.5E-05	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

LNP™ STAT-KON™ Compound PFG03EL

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL