LNP™ STAT-KON™ Compound PX11002

LNP STAT-KON PX11002 compound is based on Nylon 6 resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, Impact Modified, Flame Retardant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 6 (Nylon 6)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
Flame Retardant
Impact resistant
No PFAS intentionally added

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Building Accessory

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+04 - 1.E+10	Ω	ASTM D257

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Compliant, 94V-1 Flame Class Rating	3	mm	UL 94 by SABIC-IP

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Multiaxial Impact	20	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	75	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	10	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	255 - 265	°C
Front - Zone 3 Temperature	250 - 260	°C
Middle - Zone 2 Temperature	250 - 260	°C
Rear - Zone 1 Temperature	245 - 255	°C
Mold Temperature	55 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 5 mm/min	42	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.8	%	ISO 527
Tensile Modulus, 1 mm/min	2400	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	68	MPa	ISO 178
Flexural Modulus, 2 mm/min	2300	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Melt Volume Rate
– Melt Volume Rate, MVR at 275°C/10.0 kg	27	cm³/10 min	ISO 1133
Density	1.31	g/cm³	ISO 1183

Curve Data

view multipoint data represented visually on graphs.

You may click on the curve legends to select/unselect the curves.

Please login to view graphs, download multi-point data or literature

CAE Cards