LNP STAT-KON QD000I compound is based on Nylon 6/10 resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, High Impact.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | 1.E+02 - 1.E+04 | Ω.cm | ASTM D257 |
| Surface Resistivity | 1.E+02 - 1.E+04 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 603 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.12 - 0.2 | % | |
| Melt Temperature | 270 - 275 | °C | |
| Front - Zone 3 Temperature | 270 - 280 | °C | |
| Middle - Zone 2 Temperature | 260 - 270 | °C | |
| Rear - Zone 1 Temperature | 250 - 260 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 31 | MPa | ASTM D638 |
| Tensile Strain, break | 52.7 | % | ASTM D638 |
| Flexural Stress | 54 | MPa | ASTM D790 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.28 | % | ASTM D570 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 55 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 1.17E-04 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 1.17E-04 | 1/°C | ASTM E831 |