LNP STAT-KON RD000I compound is based on Nylon 6/6 resin containing conductive carbon powder. Added features of this grade include: Electrically Conductive, High Impact.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+01 - 1.E+06 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1810 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 150 | J/m | ASTM D256 |
| Multiaxial Impact | 20 | J | ISO 6603 |
| Instrumented Dart Impact Total Energy, 23°C | 16 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 155 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 280 - 305 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 41 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 18 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2120 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 1920 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 41 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 18 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2190 | MPa | ISO 527 |
| Flexural Stress | 62 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2020 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.15 | - | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.49 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 2 - 4 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 2 - 4 | % | ASTM D955 |
| Density | 1.15 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 0.73 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 206 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 73 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 1.1E-04 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 1.2E-04 | 1/°C | ASTM D696 |
| Thermal Conductivity | 2.8 | W/m-°C | ASTM E1530 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 191 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 68 | °C | ISO 75/Af |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+01 - 1.E+06 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 1810 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 150 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 46 | MPa | ASTM D638 |
| Tensile Strain, break | 13.5 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2120 | MPa | ASTM D638 |
| Flexural Stress | 82 | MPa | ASTM D790 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 73 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 1.21E-04 | 1/°C | ASTM E831 |
| Thermal Conductivity | 2.8 | W/m-°C | ASTM E1530 |