LNP™ STAT-KON™ Compound RE002XXP

LNP STAT-KON RE002XXP compound is based on Nylon 6/6 resin containing 10% carbon fiber. Added features of this grade include: Electrically Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 66 (Nylon 66)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Electrically Conductive
High stiffness/Strength
No PFAS intentionally added

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Electronic Components

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1E+05 - 1E+06	Ω	ASTM D257
Volume Resistivity	1E+07 - 1E+08	Ω.cm	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	32	J/m	ASTM D256
Izod Impact, unnotched, 23°C	290	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	3.5	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	21	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	3.7	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	23	kJ/m²	ISO 179/1eU
Instrumented Dart Impact Total Energy, 23°C	5.8	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	5.8	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	280 - 305	°C
Front - Zone 3 Temperature	295 - 305	°C
Middle - Zone 2 Temperature	280 - 295	°C
Rear - Zone 1 Temperature	265 - 275	°C
Mold Temperature	95 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	140	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.5	%	ASTM D638
Tensile Modulus, 5 mm/min	9600	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	210	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	7000	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	145	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.4	%	ISO 527
Tensile Modulus, 1 mm/min	9800	MPa	ISO 527
Flexural Strength, 2 mm/min	207	MPa	ISO 178
Flexural Modulus, 2 mm/min	7700	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.18	-	ASTM D792
Density	1.18	g/cm³	ISO 1183
Melt Flow Rate, 280°C/1.2 kgf	20	g/10 min	ASTM D1238
Melt Flow Rate, 280°C/2.16 kgf	35	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 280°C/1.2 kg	20	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 280°C/2.16 kg	37	cm³/10 min	ISO 1133
Water Absorption, (23°C/24hrs)	0.98	%	ISO 62-1
Moisture Absorption, (23°C/50% RH/24hrs)	0.15	%	ISO 62-4
Mold Shrinkage, flow	0.3 - 0.4	%	SABIC method
Mold Shrinkage, xflow	1.0 - 1.1	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	260	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	246	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	260	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	245	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	2.01E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	8.09E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	2.07E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	8.58E-05	1/°C	ISO 11359-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES