LNP STAT-KON RE004 compound is based on Nylon 6/6 resin containing 20% carbon fiber. Added features of this grade include: Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 523 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 64 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 52 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 280 - 305 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Mold Temperature | 95 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 219 | MPa | ASTM D638 |
| Tensile Strain, break | 4.3 | % | ASTM D638 |
| Flexural Stress | 312 | MPa | ASTM D790 |
| Flexural Modulus | 12340 | MPa | ASTM D790 |
| Tensile Stress, break | 233 | MPa | ISO 527 |
| Tensile Strain, break | 2.9 | % | ISO 527 |
| Flexural Stress | 337 | MPa | ISO 178 |
| Flexural Modulus | 14600 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.2 - 0.3 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.7 - 0.8 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.17 - 0.26 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.68 - 0.78 | % | ISO 294 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Relative Temp Index, Elec | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 52 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 218 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.6 | % | ISO 527 |
| Flexural Stress, break, 2 mm/min | 305 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 12300 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 1.2E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.12E-04 | 1/°C | ISO 11359-2 |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | >220 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |