LNP™ STAT-KON™ Compound RFD04

LNP STAT-KON* RFD04 is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added features of this material include: Electrically Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 66 (Nylon 66)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
High stiffness/Strength
No PFAS intentionally added

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+03 - 1.E+07	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	301	J/m	ASTM D4812
Izod Impact, notched, 23°C	36	J/m	ASTM D256
Multiaxial Impact	1	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	3	J	ASTM D3763
*Izod Impact, unnotched 80103 +23°C*	20	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	3	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	280 - 305	°C
Front - Zone 3 Temperature	295 - 305	°C
Middle - Zone 2 Temperature	280 - 295	°C
Rear - Zone 1 Temperature	265 - 275	°C
Mold Temperature	95 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	124	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	1.6	%	ASTM D638
Tensile Modulus, 50 mm/min	9200	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	190	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	8540	MPa	ASTM D790
Tensile Stress, break	117	MPa	ISO 527
Tensile Stress, break, 5 mm/min	119	MPa	ISO 527
Tensile Strain, break	1.3	%	ISO 527
Tensile Strain, break, 5 mm/min	1.6	%	ISO 527
Tensile Modulus, 1 mm/min	8780	MPa	ISO 527
Flexural Stress	185	MPa	ISO 178
Flexural Modulus	8600	MPa	ISO 178
Flexural Modulus, 2 mm/min	8170	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.4	-	ASTM D792
Density	1.39	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.5	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.5 - 0.7	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1 - 3	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	0.61	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.35	%	ISO 294
Density	1.39	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.75	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	259	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	248	°C	ASTM D648
CTE, -30°C to 30°C, flow	3.4E-05	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	6.1E-05	1/°C	ASTM D696
CTE, -40°C to 40°C, flow	3.22E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	6.46E-05	1/°C	ISO 11359-2
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	257	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	242	°C	ISO 75/Af

Register for High value Multi-Point Data