ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
LNP STAT-KON RX05488 compound is based on Nylon 6/6 resin containing carbon fiber, glass fiber, PTFE. Added features of this grade include: Electrically Conductive, Flame Retardant, Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 646 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 90 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 6 | J | ASTM D3763 |
Multiaxial Impact | 3 | J | ISO 6603 |
Izod Impact, unnotched 80*10*4 +23°C | 44 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 11 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.15 - 0.25 | % | |
Melt Temperature | 280 - 305 | °C | |
Front - Zone 3 Temperature | 295 - 305 | °C | |
Middle - Zone 2 Temperature | 280 - 295 | °C | |
Rear - Zone 1 Temperature | 265 - 275 | °C | |
Mold Temperature | 95 - 110 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 169 | MPa | ASTM D638 |
Tensile Strain, break | 1.6 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 24610 | MPa | ASTM D638 |
Flexural Stress | 255 | MPa | ASTM D790 |
Flexural Modulus | 14470 | MPa | ASTM D790 |
Tensile Stress, break | 175 | MPa | ISO 527 |
Tensile Strain, break | 1.8 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 18700 | MPa | ISO 527 |
Flexural Stress | 271 | MPa | ISO 178 |
Flexural Modulus | 17600 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.7 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.32 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.7 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 0.24 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 0.67 | % | ISO 294 |
Moisture Absorption (23°C / 50% RH) | 0.47 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 242 | °C | ASTM D648 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | >240 | °C | ISO 75/Af |