ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
LNP STAT-KON SX90398 compound is based on Nylon 12 resin containing stainless steel fiber. Added features of this grade include: Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | NB | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 74 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 9 | J | ASTM D3763 |
Multiaxial Impact | 20 | J | ISO 6603 |
Izod Impact, unnotched 80*10*4 +23°C | 85 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 - 6 | Hrs | |
Maximum Moisture Content | 0.12 - 0.2 | % | |
Melt Temperature | 205 | °C | |
Front - Zone 3 Temperature | 230 - 245 | °C | |
Middle - Zone 2 Temperature | 205 - 215 | °C | |
Rear - Zone 1 Temperature | 180 - 195 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield | 43 | MPa | ASTM D638 |
Tensile Stress, break | 36 | MPa | ASTM D638 |
Tensile Strain, yield | 5.3 | % | ASTM D638 |
Tensile Strain, break | 117.2 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 1900 | MPa | ASTM D638 |
Flexural Stress | 62 | MPa | ASTM D790 |
Flexural Modulus | 1770 | MPa | ASTM D790 |
Tensile Stress, yield | 38 | MPa | ISO 527 |
Tensile Stress, break | 35 | MPa | ISO 527 |
Tensile Modulus, 1 mm/min | 1440 | MPa | ISO 527 |
Flexural Stress | 50 | MPa | ISO 178 |
Flexural Modulus | 1760 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.102 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.2 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 1.1 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 1.7 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 1.12 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 1.7 | % | ISO 294 |
Density | 1.09 | g/cm³ | ISO 1183 |
Moisture Absorption (23°C / 50% RH) | 0.3 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 113 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 67 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 1.03E-04 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 9.93E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 1.04E-04 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 9.94E-05 | 1/°C | ISO 11359-2 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 104 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 73 | °C | ISO 75/Af |