LNP™ STAT-KON™ Compound TX06488

LNP STAT-KON TX06488 compound is based on Polyurethane (TPU) resin containing conductive carbon powder. Added features of this grade include: Excellent Ductility, Electrically Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyurethane, Unspecified (PUR, Unspecified)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
Impact resistant
No PFAS intentionally added

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Wire & cable

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+02 - 1.E+05	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Multiaxial Impact	41	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	39	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	95 - 105	°C
Drying Time	2	Hrs
Maximum Moisture Content	0.03	%
Melt Temperature	210	°C
Nozzle Temperature	205 - 225	°C
Front - Zone 3 Temperature	200 - 220	°C
Middle - Zone 2 Temperature	195 - 215	°C
Rear - Zone 1 Temperature	195 - 210	°C
Mold Temperature	15 - 45	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Shot to Cylinder Size	40 - 80	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	19	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	18	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	388	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	392	%	ASTM D638
Tensile Modulus, 5 mm/min	60	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	60	MPa	ASTM D790
Hardness, Shore A	90	-	ASTM D2240

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.28	-	ASTM D792
Density	1.28	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.67	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.8 - 1	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.4 - 0.6	%	ASTM D955
Moisture Absorption (23°C / 50% RH)	0.89	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	23	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	23	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	23	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	23	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES