ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 9.E+07 | Ω | ASTM D257 |
LNP STAT-KON WX11322 compound is based on Polybutylene Terephthalate (PBT) resin containing glass fiber and carbon fiber. Added features of this grade include: Electrically Conductive, Flame Retardant, Low Warpage.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 9.E+07 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 2 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 78 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 12 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 250 - 265 | °C | |
Nozzle Temperature | 245 - 260 | °C | |
Front - Zone 3 Temperature | 250 - 265 | °C | |
Middle - Zone 2 Temperature | 245 - 260 | °C | |
Rear - Zone 1 Temperature | 240 - 255 | °C | |
Mold Temperature | 65 - 90 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 50 - 80 | rpm | |
Shot to Cylinder Size | 40 - 80 | % | |
Vent Depth | 0.025 - 0.038 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield | 143 | MPa | SABIC - Japan Method |
Tensile Strain, break | 9 | % | SABIC - Japan Method |
Flexural Stress, yield, 6.4 mm | 208 | MPa | ASTM D790 |
Flexural Modulus, 6.4 mm | 11600 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.54 | - | ASTM D792 |
Mold Shrinkage, flow, 1.5-3.2 mm | 0.17 | % | SABIC method |
Mold Shrinkage, xflow, 1.5-3.2 mm | 0.55 | % | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 6.4 mm, unannealed | 205 | °C | ASTM D648 |
Relative Temp Index, Elec | 75 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 75 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 75 | °C | UL 746B |