LNP™ STAT-KON™ Compound ZD000XXR

LNP STAT-KON ZD000XXR compound is based on Polyphenylene Ether/Polystyrene (PPE/PS) blend which is electrically conductive with improved toughness and reduced carbon sloughing. This is targeted for applications like IC trays and packaging for semi-conductor industry.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dimensional stability
Electrically Conductive
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Material Handling

Applications

Possible usage of material

Industrial Material Handling
Semiconductor
ic tray
disk caddy
process tray
jedec tray

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.6E+6	Ω	ASTM D257
Volume Resistivity	7.2E+6	Ω.cm	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	77.5	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1020	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	6.68	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	43.91	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	6.6	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	61.4	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110 - 120	°C
Drying Time	3 - 5	Hrs
Melt Temperature	300 - 310	°C
Nozzle Temperature	300 - 310	°C
Front - Zone 3 Temperature	300 - 310	°C
Middle - Zone 2 Temperature	300 - 310	°C
Rear - Zone 1 Temperature	300 - 310	°C
Mold Temperature	110 - 130	°C
Back Pressure	0.1 - 0.3	MPa
Screw Speed	90 - 110	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 50 mm/min	60.3	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	5.2	%	ASTM D638
Tensile Modulus, 50 mm/min	3195	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	107	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	3040	MPa	ASTM D790
Tensile Stress, break, 50 mm/min	59.1	MPa	ISO 527
Tensile Strain, break, 50 mm/min	4.86	%	ISO 527
Tensile Modulus, 1 mm/min	3077	MPa	ISO 527
Flexural Strength, 2 mm/min	107	MPa	ISO 178
Flexural Modulus, 2 mm/min	3245	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.17	-	ASTM D792
Melt Volume Rate, MVR at 300°C/10.0 kg	7.57	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.78	%	SABIC method
Mold Shrinkage, xflow	0.74	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	177	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	165	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	176	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	162	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	6.4E-5	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	7.6E-5	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	6.0E-5	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	7.6E-5	1/°C	ISO 11359-2
Vicat Softening Temp, Rate A/50	193	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	182	°C	ISO 306

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES