LNP STAT-KON ZE0039 compound is based on Polyphenylene Ether / Polystyrene (PPE/PS) blend containing 15% carbon fiber. Added features of this grade include: Electrically Conductive , Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+02 - 1.E+04 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 267 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 48 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 11 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 18 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 300 - 305 | °C | |
| Front - Zone 3 Temperature | 300 - 310 | °C | |
| Middle - Zone 2 Temperature | 290 - 300 | °C | |
| Rear - Zone 1 Temperature | 275 - 290 | °C | |
| Mold Temperature | 80 - 110 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 112 | MPa | ASTM D638 |
| Tensile Stress, break | 112 | MPa | ASTM D638 |
| Tensile Strain, yield | 1.2 | % | ASTM D638 |
| Tensile Strain, break | 1.2 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 11720 | MPa | ASTM D638 |
| Flexural Stress | 117 | MPa | ASTM D790 |
| Flexural Modulus | 8960 | MPa | ASTM D790 |
| Tensile Stress, yield | 105 | MPa | ISO 527 |
| Tensile Stress, break | 105 | MPa | ISO 527 |
| Tensile Strain, yield | 1.1 | % | ISO 527 |
| Tensile Strain, break | 1.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 10970 | MPa | ISO 527 |
| Flexural Stress | 150 | MPa | ISO 178 |
| Flexural Modulus | 10600 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.1 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 0.1 - 0.2 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.2 - 0.4 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.09 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.3 | % | ISO 294 |
| Density | 1.2 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 112 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 103 | °C | ASTM D648 |
| CTE, -30°C to 30°C, flow | 2.9E-05 | 1/°C | ASTM D696 |
| CTE, -30°C to 30°C, xflow | 4.7E-05 | 1/°C | ASTM D696 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 113 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 106 | °C | ISO 75/Af |