LNP™ STAT-LOY™ Compound 63000CT

LNP STAT-LOY 63000CT compound is based on Polycarbonate / Polyester alloy containing proprietary additives targeted for advanced semiconductor packaging applications. Added features of this grade include: LNP Clean Compounding Technology, Permanently Anti-Static, Translucent.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + Polyester (PC+Polyester)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Antistatic
Low ionics/Outgassing/Liquid particle count
No PFAS intentionally added
Transparent/Translucent

Industry

Material previously used in

Electrical
Electronic Components
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Data Management
Electronic Components
Personal Computing
Semiconductor
blanks case
blanks
photomask
reticle
mask
media
hard drive
hdd

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+11 - 5.E+12	Ω	ASTM D257
Volume Resistivity	1.E+11 - 5.E+12	Ω.cm	ASTM D257
Static Decay, 5000V to <50V	<2	Seconds	FTMS101B

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	580	J/m	ASTM D256
Charpy Impact, notched, 23°C	69	kJ/m²	ISO 179/2C

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	90 - 95	°C
Drying Time	6 - 8	Hrs
Melt Temperature	230 - 250	°C
Nozzle Temperature	230 - 250	°C
Front - Zone 3 Temperature	230 - 250	°C
Middle - Zone 2 Temperature	225 - 240	°C
Rear - Zone 1 Temperature	220 - 230	°C
Mold Temperature	40 - 50	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	35	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	200	%	ASTM D638
Tensile Modulus, 5 mm/min	1160	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	50	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	1160	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	34	MPa	ISO 527
Tensile Strain, break, 5 mm/min	140	%	ISO 527
Tensile Modulus, 1 mm/min	1180	MPa	ISO 527
Flexural Modulus, 2 mm/min	1140	MPa	ISO 178

OPTICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Light Transmission, 2.54 mm	81	%	ASTM D1003
Haze, 2.54 mm	10	%	ASTM D1003

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.16	g/cm³	ASTM D792
Mold Shrinkage, flow	0.6	%	SABIC method
Mold Shrinkage, xflow	0.6	%	SABIC method
Melt Flow Rate, 260°C/2.16 kgf	16	g/10 min	ASTM D1238
Moisture Absorption (23°C / 50% RH)	0.7	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 6.4 mm, unannealed	83	°C	ASTM D648
HDT, 1.82 MPa, 6.4 mm, unannealed	73	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	68	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES