LNP™ STAT-LOY™ Compound A3000TC

LNP STAT-LOY A3000TC compound is a ABS resin based electrically conductive material with transparency, low surface resistivity and high cleanliness. Added features of this grade include LNP Clean Compounding Technology. This material is targeted for jigs, fixtures and boxes for semi-conductor/electronics handling industry.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Acrylonitrile Butadiene Styrene (ABS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Antistatic
Low ionics/Outgassing/Liquid particle count
No PFAS intentionally added
Transparent/Translucent

Industry

Material previously used in

Electrical
Electronic Components
Material Handling

Applications

Possible usage of material

Electronic Components

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	6.3E+9	Ω	ASTM D257
Volume Resistivity	3.1E+10	Ω.cm	ASTM D257
Dielectric Constant, 1.1 GHz	2.82	-	SABIC method
Dissipation Factor, 1.1 GHz	0.03593	-	SABIC method
Dielectric Constant, 1.9 GHz	2.81	-	SABIC method
Dissipation Factor, 1.9 GHz	0.03966	-	SABIC method
Dielectric Constant, 5 GHz	2.75	-	SABIC method
Dissipation Factor, 5 GHz	0.03223	-	SABIC method
Dielectric Constant, 10 GHz	2.76	-	SABIC method
Dissipation Factor, 10 GHz	0.02348	-	SABIC method
Dielectric Constant, 20 GHz	2.62	-	SABIC method
Dissipation Factor, 20 GHz	0.03636	-	SABIC method

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	138	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1610	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	11.6	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	108.3	kJ/m²	ISO 180/1U
Charpy
– 23°C, V-notch Edgew 80104 sp=62mm	12.25	kJ/m²	ISO 179/1eA
– 23°C, Unnotch Edgew 80104 sp=62mm	95.64	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	75 - 80	°C
Drying Time	6 - 8	Hrs
Melt Temperature	240 - 260	°C
Nozzle Temperature	240 - 260	°C
Front - Zone 3 Temperature	240 - 260	°C
Middle - Zone 2 Temperature	240 - 260	°C
Rear - Zone 1 Temperature	240 - 260	°C
Mold Temperature	40 - 60	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 50 mm/min	29.8	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	24.3	%	ASTM D638
Tensile Modulus, 50 mm/min	2040	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	55.6	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	1800	MPa	ASTM D790
Tensile Stress, break, 50 mm/min	30	MPa	ISO 527
Tensile Strain, break, 50 mm/min	20.3	%	ISO 527
Tensile Modulus, 1 mm/min	2010	MPa	ISO 527
Flexural Strength, 2 mm/min	55.1	MPa	ISO 178
Flexural Modulus, 2 mm/min	1874	MPa	ISO 178

OPTICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Light Transmission, 1.0 mm	88.4	%	ASTM D1003
Haze, 1.0 mm	8.3	%	ASTM D1003

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.11	-	ASTM D792
Melt Flow Rate, 260°C/1.2 kgf	12.1	g/10 min	ASTM D1238
Water Absorption, (23°C/24hrs)	0.17	%	ASTM D570
Moisture Absorption (23°C / 50% RH)	0.58	%	ISO 62
Mold Shrinkage, flow	0.73	%	SABIC method
Mold Shrinkage, xflow	0.84	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	79.2	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	68.9	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	75.8	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	65.3	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	9.1E-5	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	11.5E-5	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	9.0E-5	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	12.1E-5	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/120	80.6	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	80.9	°C	ISO 306

Register for High value Multi-Point Data