LNP™ STAT-LOY™ Compound A3000TXB

LNP STAT-LOY A3000TXB compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing proprietary fillers. Added features of this grade include: Permanently Anti-Static, Transparent, Bio-assessed to ISO 10993, Besides healthcare, this material is also targeted for food contact applications (excluding Europe).

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Acrylonitrile Butadiene Styrene (ABS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Antistatic
Biocompatability-ISO10993
Healthcare/Formula lock
No PFAS intentionally added
Transparent/Translucent

Industry

Material previously used in

Food & Beverage
General Healthcare
Home Appliances
Industrial Packaging
Patient Testing
Pharmaceutical Packaging and Drug Delivery
Surgical devices
Water Management

Applications

Possible usage of material

Non-LED Lighting
Pharmaceutical Manufacturing
Pharmaceutical Packaging & Drug Delivery

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.E+10 - 1.E+12	Ω.cm	ASTM D257
Surface Resistivity	1.E+09 - 1.E+11	Ω	ASTM D257
Static Decay, 5000V to <50V	<1	Seconds	FTMS101B

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	131	J/m	ASTM D256
Multiaxial Impact	33	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	20	J	ASTM D3763
*Izod Impact, notched 80104 +23°C*	14	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	70 - 80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.05 - 0.1	%
Melt Temperature	200 - 210	°C
Front - Zone 3 Temperature	205 - 215	°C
Middle - Zone 2 Temperature	195 - 205	°C
Rear - Zone 1 Temperature	180 - 195	°C
Mold Temperature	10 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	38	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	27	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	4	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	31	%	ASTM D638
Tensile Modulus, 5 mm/min	1660	MPa	ASTM D638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	54	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	1630	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	37	MPa	ISO 527
Tensile Stress, break, 5 mm/min	26	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	4	%	ISO 527
Tensile Strain, break, 5 mm/min	29	%	ISO 527
Tensile Modulus, 1 mm/min	1550	MPa	ISO 527
Flexural Stress	49	MPa	ISO 178
Flexural Modulus, 2 mm/min	1490	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.09	-	ASTM D792
Density	1.08	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.54	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.4 - 0.6	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.6 - 0.8	%	ASTM D955
Moisture Absorption (23°C / 50% RH)	0.81	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	78	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	66	°C	ASTM D648
CTE, -30°C to 30°C, flow	1.E-05	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	1.09E-04	1/°C	ASTM D696
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	77	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	66	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES