LNP™ STAT-LOY™ Compound A3000XXP

LNP STAT-LOY A3000XXP compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing proprietary fillers. Added features of this grade include: Permanently Anti-Static.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Acrylonitrile Butadiene Styrene (ABS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Antistatic
No PFAS intentionally added

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+10 - 1.E+12	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	91	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1066	J/m	ASTM D4812
*Izod Impact, unnotched 80104 +23°C*	135	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	12	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	70 - 80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.05 - 0.1	%
Melt Temperature	200 - 210	°C
Front - Zone 3 Temperature	205 - 215	°C
Middle - Zone 2 Temperature	195 - 205	°C
Rear - Zone 1 Temperature	180 - 195	°C
Mold Temperature	10 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	1800	MPa	ISO 527
Tensile Stress, yield, 50 mm/min	40	MPa	ISO 527
Tensile Stress, break, 50 mm/min	27	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	3.6	%	ISO 527
Tensile Nominal Strain, break, 50 mm/min	17.9	%	ISO 527
Flexural Modulus, 2 mm/min	1800	MPa	ISO 178
Flexural Strength, 2 mm/min	56	MPa	ISO 178
Tensile Modulus, 50 mm/min	1900	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	40	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	27	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	3.7	%	ASTM D638
Tensile Nominal Strain, brk, Type I, 50 mm/min	14.6	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	1900	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	59	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.08	g/cm³	ISO 1183
Mold Shrinkage, flow	0.5 - 0.7	%	SABIC method
Melt Flow Rate, 230°C/5 kgf	19	g/10 min	ASTM D1238
Mold Shrinkage, xflow	0.6 - 0.8	%	SABIC method
Moisture Absorption, (23°C/50% RH/Equilibrium)	0.5	%	ISO 62-4
Moisture Absorption, (23°C/50% RH/24hrs)	0.2	%	ISO 62-4

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	90	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	75	°C	ASTM D648
Vicat Softening Temp, Rate B/50	94	°C	ISO 306
Vicat Softening Temp, Rate B/120	95	°C	ISO 306
CTE, 23°C to 60°C, flow	1.0E-04	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	1.1E-04	1/°C	ISO 11359-2
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	92	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	81	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES