LNP™ STAT-LOY™ Compound D30009

LNP STAT-LOY D30009 compound is a Polycarbonate (PC) resin based electrically conductive material with colorability, low surface resistivity, flame retardant, and good surface quality. This material is targeted for explosive proof application.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Electrically Conductive
Flame Retardant

Industry

Material previously used in

Electronic Components

Applications

Possible usage of material

Electronic Components

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	5.0E+10	Ω/sq	ASTM D257
Volume Resistivity	4.3E+10	Ω.cm	ASTM D257
Surface Resistance	9.5E+08	Ω	ASTM D257
Dielectric Constant, 1.1 GHz	3.3	-	SABIC method
Dissipation Factor, 1.1 GHz	0.0355	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	1.5	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	600	J/m	ASTM D256
Izod Impact, notched, -20°C	230	J/m	ASTM D256
Izod Impact, notched, -30°C	100	J/m	ASTM D256
*Izod Impact, notched 80103 +23°C*	62	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	10	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 +23°C*	65	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	13	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	83	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	9	kJ/m²	ISO 179/1eA
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	89	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	10	kJ/m²	ISO 179/1eA
Instrumented Dart Impact Total Energy, 23°C	39	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	70 - 80	°C
Drying Time	6 - 8	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	225 - 255	°C
Nozzle Temperature	225 - 255	°C
Front - Zone 3 Temperature	225 - 255	°C
Middle - Zone 2 Temperature	220 - 250	°C
Rear - Zone 1 Temperature	220 - 250	°C
Mold Temperature	40 - 60	°C
Back Pressure	0.1 - 0.5	MPa
Screw Speed	30 - 70	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	46	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	30	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	4.5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	>20	%	ASTM D638
Tensile Modulus, 5 mm/min	1820	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	70	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	1800	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	45	MPa	ISO 527
Tensile Stress, break, 50 mm/min	30	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	4.5	%	ISO 527
Tensile Strain, break, 50 mm/min	>20	%	ISO 527
Tensile Modulus, 1 mm/min	1800	MPa	ISO 527
Flexural Strength, 2 mm/min	68	MPa	ISO 178
Flexural Modulus, 2 mm/min	1780	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.33	-	ASTM D792
Melt Flow Rate, 260°C/1.2 kgf	10	g/10 min	ASTM D1238
Melt Flow Rate, 260°C/2.16 kgf	18.5	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/1.2 kg	9	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 260°C/2.16 kg	16	cm³/10 min	ISO 1133
Water Absorption, (23°C/saturated)	0.85	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.13	%	ISO 62
Mold Shrinkage, flow, 3.2 mm	0.3 - 0.6	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.3 - 0.6	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	122	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	106	°C	ASTM D648
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	123	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	103	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	7.20E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	9.70E-05	1/°C	ISO 11359-2
Vicat Softening Temp, Rate A/50	138	°C	ISO 306
Vicat Softening Temp, Rate B/50	113	°C	ISO 306
Vicat Softening Temp, Rate B/120	113	°C	ISO 306

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES