ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+10 - 1.E+12 | Ω.cm | ASTM D257 |
Surface Resistivity | 1.E+10 - 1.E+12 | Ω | ASTM D257 |
LNP STAT-LOY KX01002 compound is based on POM (Acetal) copolymer resin containing proprietary fillers. Added features of this grade include: Permanently Anti-Static.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+10 - 1.E+12 | Ω.cm | ASTM D257 |
Surface Resistivity | 1.E+10 - 1.E+12 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 14 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 195 - 205 | °C | |
Front - Zone 3 Temperature | 200 - 210 | °C | |
Middle - Zone 2 Temperature | 190 - 200 | °C | |
Rear - Zone 1 Temperature | 175 - 190 | °C | |
Mold Temperature | 70 - 95 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 5 mm/min | 43 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 15.8 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 1600 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 52 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 1600 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow | 2.8 | % | SABIC method |
Density | 1.35 | g/cm³ | ISO 1183 |
Melt Volume Rate, MVR at 190°C/10.0 kg | 16 | cm³/10 min | ISO 1133 |
Water Absorption, (23°C/24hrs) | 4.8 | % | ISO 62-1 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 136 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 64 | °C | ISO 75/Af |