LNP STAT-LOY KX09024 compound is based on POM (Acetal) copolymer resin containing proprietary fillers. Added features of this grade include: Permanently Anti-Static.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | 1.E+08 - 1.E+10 | Ω.cm | ASTM D257 |
| Surface Resistivity | 1.E+08 - 1.E+10 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 195 - 205 | °C | |
| Front - Zone 3 Temperature | 200 - 210 | °C | |
| Middle - Zone 2 Temperature | 190 - 200 | °C | |
| Rear - Zone 1 Temperature | 175 - 190 | °C | |
| Mold Temperature | 70 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Strain, break, 5 mm/min | 12 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 48 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 1400 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 2.8 | % | SABIC method |
| Density | 1.27 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 1.44E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.59E-04 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 136 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 67 | °C | ISO 75/Af |