LNP™ STAT-LOY™ Compound KX96821

LNP STAT-LOY KX96821 compound is based on POM (Acetal) copolymer resin containing proprietary fillers. Added features of this grade include: Permanently Anti-Static.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Acetal (POM) Copolymer

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Antistatic
No PFAS intentionally added

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Plumbing

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+09 - 1.E+11	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812
Izod Impact, notched, 23°C	133	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	32	J	ASTM D3763
Multiaxial Impact	18	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	13	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Melt Temperature	195 - 205	°C
Front - Zone 3 Temperature	200 - 210	°C
Middle - Zone 2 Temperature	190 - 200	°C
Rear - Zone 1 Temperature	175 - 190	°C
Mold Temperature	70 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	44	MPa	ASTM D638
Tensile Stress, break	34	MPa	ASTM D638
Tensile Strain, yield	14.8	%	ASTM D638
Tensile Strain, break	54.4	%	ASTM D638
Tensile Modulus, 50 mm/min	1850	MPa	ASTM D638
Flexural Stress	54	MPa	ASTM D790
Flexural Modulus	1600	MPa	ASTM D790
Tensile Stress, yield	43	MPa	ISO 527
Tensile Stress, break	39	MPa	ISO 527
Tensile Strain, yield	11.9	%	ISO 527
Tensile Strain, break	32.3	%	ISO 527
Tensile Modulus, 1 mm/min	1600	MPa	ISO 527
Flexural Stress	40	MPa	ISO 178
Flexural Modulus	1540	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.32	g/cm³	ASTM D792
Mold Shrinkage, flow, 24 hrs	1.9	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1.8	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	1.88	%	ISO 294
Moisture Absorption, (23°C/50% RH/24 hrs)	3.06	%	ASTM D570
Mold Shrinkage, xflow, 24 hrs	1.82	%	ISO 294
Melt Volume Rate, MVR at 190°C/10.0 kg	15	cm³/10 min	ISO 1133
Density	1.32	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	82	°C	ASTM D648
CTE, -40°C to 40°C, flow	1.35E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.49E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.35E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.49E-04	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	73	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES