LNP™ STAT-LOY™ Compound M3000

LNP STAT-LOY M3000 compound is based on unfilled Polypropylene (PP) resin containing proprietary fillers. Added features of this grade include: Permanently Anti-Static.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polypropylene, Unspecified (PP, Unspecified)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Antistatic
No PFAS intentionally added

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Conveyor
Data Management
Electronic Components
Enclosures
Vacuum Cleaner
atm
household appliance
domestic appliance

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+09 - 1.E+11	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812
Izod Impact, notched, 23°C	69	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	7	J	ASTM D3763
Multiaxial Impact	5	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	10	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	70 - 80	°C
Drying Time	4	Hrs
Melt Temperature	190 - 200	°C
Front - Zone 3 Temperature	200 - 210	°C
Middle - Zone 2 Temperature	195 - 205	°C
Rear - Zone 1 Temperature	180 - 195	°C
Mold Temperature	30 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	28	MPa	ASTM D638
Tensile Strain, yield	9.6	%	ASTM D638
Tensile Strain, break	47	%	ASTM D638
Tensile Modulus, 50 mm/min	1390	MPa	ASTM D638
Flexural Stress	40	MPa	ASTM D790
Flexural Modulus	1440	MPa	ASTM D790
Tensile Stress, yield	28	MPa	ISO 527
Tensile Strain, yield	8	%	ISO 527
Tensile Strain, break	98.2	%	ISO 527
Tensile Modulus, 1 mm/min	1350	MPa	ISO 527
Flexural Stress	32	MPa	ISO 178
Flexural Modulus	1360	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	0.95	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.85	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	1.4	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1.3	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	1.35	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.33	%	ISO 294
Density	0.95	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	100	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	56	°C	ASTM D648
CTE, -40°C to 40°C, flow	1.1E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.28E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	1.1E-04	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.28E-04	1/°C	ISO 11359-2
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	103	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	59	°C	ISO 75/Af

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+09 - 1.E+11	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	10	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	70 - 80	°C
Drying Time	4	Hrs
Melt Temperature	190 - 200	°C
Front - Zone 3 Temperature	200 - 210	°C
Middle - Zone 2 Temperature	195 - 205	°C
Rear - Zone 1 Temperature	180 - 195	°C
Mold Temperature	30 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 50 mm/min	28	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	7.4	%	ISO 527
Tensile Strain, break, 50 mm/min	>100	%	ISO 527
Tensile Modulus, 1 mm/min	1350	MPa	ISO 527
Flexural Stress, break, 2 mm/min	34	MPa	ISO 178
Flexural Modulus, 2 mm/min	1200	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	0.95	g/cm³	ISO 1183

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
CTE, 23°C to 60°C, flow	1.21E-04	1/°C	ISO 11359-2
CTE, 23°C to 60°C, xflow	1.51E-04	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	59	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

LNP™ STAT-LOY™ Compound M3000

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Related Documents

Technical Data Sheets

Register for High value Multi-Point Data