LNP™ STAT-LOY™ Compound M3000C

LNP STAT-LOY M3000C compound is based on unfilled Polypropylene (PP) resin containing proprietary fillers. Added features of this grade include: LNP Clean Compounding Technology, Permanently Anti-Static.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polypropylene, Unspecified (PP, Unspecified)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Antistatic
Low ionics/Outgassing/Liquid particle count
No PFAS intentionally added

Industry

Material previously used in

Electrical
Electronic Components
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Industrial Material Handling
Semiconductor

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+10 - 1.E+12	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	75	J/m	ASTM D256
Multiaxial Impact	25	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	29	J	ASTM D3763
*Izod Impact, notched 80104 +23°C*	6	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	70 - 80	°C
Drying Time	4	Hrs
Melt Temperature	190 - 200	°C
Front - Zone 3 Temperature	200 - 210	°C
Middle - Zone 2 Temperature	195 - 205	°C
Rear - Zone 1 Temperature	180 - 195	°C
Mold Temperature	30 - 50	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 50 mm/min	18	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	689	%	ASTM D638
Tensile Modulus, 50 mm/min	760	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	24	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	860	MPa	ASTM D790
Tensile Stress, break, 50 mm/min	24	MPa	ISO 527
Tensile Strain, break, 50 mm/min	690	%	ISO 527
Tensile Modulus, 1 mm/min	1180	MPa	ISO 527
Flexural Strength, 2 mm/min	38	MPa	ISO 178
Flexural Modulus, 2 mm/min	1960	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	0.93	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.16	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	1 - 2	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1 - 2	%	ASTM D955
Density	0.93	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.16	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	74	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	49	°C	ASTM D648
CTE, -30°C to 30°C, flow	1.28E-04	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	1.31E-04	1/°C	ASTM D696
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	75	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	49	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES