LNP STAT-LOY NX03583 compound is based on Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend containing proprietary fillers. Added features of this grade include: Permanently Anti-Static, Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+10 - 1.E+12 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 640 | J/m | ASTM D256 |
| Instrumented Dart Impact Energy @ peak, 23°C | 38 | J | ASTM D3763 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 200 - 230 | °C | |
| Front - Zone 3 Temperature | 220 - 230 | °C | |
| Middle - Zone 2 Temperature | 210 - 220 | °C | |
| Rear - Zone 1 Temperature | 200 - 210 | °C | |
| Mold Temperature | 40 - 55 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 56 | MPa | ASTM D638 |
| Tensile Stress, break | 49 | MPa | ASTM D638 |
| Tensile Strain, yield | 5 | % | ASTM D638 |
| Tensile Strain, break | 100 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2150 | MPa | ASTM D638 |
| Flexural Stress | 84 | MPa | ASTM D790 |
| Flexural Modulus | 2150 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 99 | °C | ASTM D648 |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |