ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+10 - 1.E+12 | Ω | ASTM D257 |
LNP STAT-LOY P3000U compound is based on Nylon 6 resin containing proprietary fillers. Added features of this grade include: Permanently Anti-Static, UV - Stabilized.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+10 - 1.E+12 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 80 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.15 - 0.25 | % | |
Melt Temperature | 265 - 275 | °C | |
Front - Zone 3 Temperature | 275 - 290 | °C | |
Middle - Zone 2 Temperature | 265 - 275 | °C | |
Rear - Zone 1 Temperature | 250 - 260 | °C | |
Mold Temperature | 80 - 95 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 50 mm/min | 56 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 44 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 3.6 | % | ISO 527 |
Flexural Stress, yield, 2 mm/min | 59 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 1800 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage, flow | 0.8 | % | SABIC method |
Density | 1.17 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/24hrs) | 6.3 | % | ISO 62-1 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 162 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 55 | °C | ISO 75/Af |