LNP™ STAT-LOY™ Compound PF306

LNP STAT-LOY PF306 compound is based on Nylon 6 resin containing 30% glass fiber. Added features of this grade include: Permanently Anti-Static.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 6 (Nylon 6)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Antistatic

Industry

Material previously used in

Electronic Components
Material Handling

Applications

Possible usage of material

Fuel Handling
Personal Computing
fuel line connector
fuel line clip
filter housing
tank inlet
switch
bezel

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+09 - 1.E+11	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	7	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	45	kJ/m²	ISO 180/1U
Multiaxial Impact	6	J	ISO 6603
Izod Impact, notched, 23°C	101	J/m	ASTM D256
Izod Impact, unnotched, 23°C	955	J/m	ASTM D4812
Instrumented Dart Impact Energy @ peak, 23°C	17	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	265 - 275	°C
Front - Zone 3 Temperature	275 - 290	°C
Middle - Zone 2 Temperature	265 - 275	°C
Rear - Zone 1 Temperature	250 - 260	°C
Mold Temperature	80 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	83	MPa	ISO 527
Tensile Stress, break	83	MPa	ISO 527
Tensile Strain, yield	2.7	%	ISO 527
Tensile Strain, break	2.8	%	ISO 527
Tensile Modulus, 1 mm/min	7470	MPa	ISO 527
Flexural Stress	106	MPa	ISO 178
Flexural Modulus	6000	MPa	ISO 178
Tensile Stress, yield	93	MPa	ASTM D638
Tensile Stress, break	93	MPa	ASTM D638
Tensile Strain, yield	2.7	%	ASTM D638
Tensile Strain, break	2.8	%	ASTM D638
Tensile Modulus, 50 mm/min	7580	MPa	ASTM D638
Flexural Stress	96	MPa	ASTM D790
Flexural Modulus	5510	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.39	g/cm³	ISO 1183
Mold Shrinkage, flow, 24 hrs	0.28	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.82	%	ISO 294
Density	1.39	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	5.1	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.2 - 0.4	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.7 - 0.9	%	ASTM D955

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	201	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	182	°C	ISO 75/Af
CTE, -40°C to 40°C, flow	4.0E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	1.19E-04	1/°C	ISO 11359-2
HDT, 0.45 MPa, 3.2 mm, unannealed	202	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	185	°C	ASTM D648
CTE, -40°C to 40°C, flow	3.96E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.19E-04	1/°C	ASTM E831

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES