LNP™ STAT-LOY™ Compound YX02589C

LNP STAT-LOY YX02589C compound is based on Polyester Elastomer resin containing proprietary fillers. Added features of this grade include: Permanently Anti-Static, LNP Clean Compounding Technology.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Thermoplastic Polyester Elastomer (TPEE)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Antistatic
Low ionics/Outgassing/Liquid particle count
No PFAS intentionally added

Industry

Material previously used in

Electrical
Electronic Components
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Data Management
Semiconductor

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Surface Resistivity	1.E+10 - 1.E+13	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Multiaxial Impact	25	J	ISO 6603
Instrumented Dart Impact Total Energy, 23°C	18	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.1	%
Melt Temperature	215 - 240	°C
Front - Zone 3 Temperature	225 - 240	°C
Middle - Zone 2 Temperature	205 - 215	°C
Rear - Zone 1 Temperature	180 - 195	°C
Mold Temperature	25 - 55	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	6	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	71.4	%	ASTM D638
Tensile Modulus, 5 mm/min	30	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	40	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	6	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	161.7	%	ISO 527
Tensile Modulus, 1 mm/min	40	MPa	ISO 527
Flexural Stress	2	MPa	ISO 178
Flexural Modulus, 2 mm/min	40	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.08	-	ASTM D792
Density	1.086	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	5.5	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.61	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.65	%	ASTM D955
Moisture Absorption (23°C / 50% RH)	8.5	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
CTE, -30°C to 30°C, flow	2.45E-04	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	2.89E-04	1/°C	ASTM D696

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES