LNP™ THERMOCOMP™ Compound 2F005

LNP THERMOCOMP 2F005 compound is based on Ethylene Tetrafluoroethylene (ETFE) resin containing 25% glass fiber.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Ethylene Tetrafluoroethylene Copolymer (ETFE)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength

Industry

Material previously used in

Electronic Components
Energy Management
Material Handling

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	44	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	90	kJ/m²	ISO 180/1U
Multiaxial Impact	10	J	ISO 6603
Izod Impact, notched, 23°C	529	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1600	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	21	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Melt Temperature	315	°C
Front - Zone 3 Temperature	325 - 340	°C
Middle - Zone 2 Temperature	300 - 325	°C
Rear - Zone 1 Temperature	280 - 300	°C
Mold Temperature	90 - 120	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 5 mm/min	61	MPa	ISO 527
Tensile Stress, break, 5 mm/min	60	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	6.6	%	ISO 527
Tensile Strain, break, 5 mm/min	7	%	ISO 527
Tensile Modulus, 1 mm/min	5670	MPa	ISO 527
Flexural Stress	87	MPa	ISO 178
Flexural Modulus, 2 mm/min	5200	MPa	ISO 178
Tensile Stress, yld, Type I, 5 mm/min	61	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	59	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	7	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	8.1	%	ASTM D638
Tensile Modulus, 50 mm/min	6190	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	5480	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Moisture Absorption (23°C / 50% RH)	0.02	%	ISO 62
Specific Gravity	1.87	-	ASTM D792
Density	1.87	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.01	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	1 - 3	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	2 - 4	%	ASTM D955

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	232	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	132	°C	ISO 75/Af
HDT, 0.45 MPa, 3.2 mm, unannealed	248	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	190	°C	ASTM D648
CTE, -30°C to 30°C, flow	6.10E-05	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	6.40E-05	1/°C	ASTM D696

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES