LNP™ THERMOCOMP™ Compound 2Z004

LNP THERMOCOMP 2Z004 compound is based on Ethylene Tetrafluoroethylene (ETFE) resin containing 20% milled glass.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Ethylene Tetrafluoroethylene Copolymer (ETFE)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dimensional stability
Impact resistant
Low Warpage

Industry

Material previously used in

Electronic Components
Energy Management
Material Handling

Applications

Possible usage of material

Enclosures

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1340	J/m	ASTM D4812
Izod Impact, notched, 23°C	615	J/m	ASTM D256
Instrumented Dart Impact Total Energy, 23°C	26	J	ASTM D3763
*Izod Impact, unnotched 80104 +23°C*	119	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	37	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Melt Temperature	315	°C
Front - Zone 3 Temperature	325 - 340	°C
Middle - Zone 2 Temperature	300 - 325	°C
Rear - Zone 1 Temperature	280 - 300	°C
Mold Temperature	90 - 120	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 5 mm/min	29	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	21	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	23	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	53	%	ASTM D638
Tensile Modulus, 5 mm/min	1700	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	1280	MPa	ASTM D790
Tensile Stress, yield, 5 mm/min	27	MPa	ISO 527
Tensile Stress, break, 5 mm/min	22	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	22	%	ISO 527
Tensile Strain, break, 5 mm/min	78	%	ISO 527
Tensile Modulus, 1 mm/min	1510	MPa	ISO 527
Flexural Strength, 2 mm/min	24	MPa	ISO 178
Flexural Modulus, 2 mm/min	1210	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.84	-	ASTM D792
Density	1.83	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.01	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	1 - 2	%	ASTM D955

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	88	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	52	°C	ASTM D648
CTE, -30°C to 30°C, flow	8.E-05	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	8.7E-05	1/°C	ASTM D696
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	89	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	50	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES