LNP™ THERMOCOMP™ Compound 5C003

LNP THERMOCOMP 5C003 compound is based on Polyvinylidene Fluoride (PVDF) resin containing 15% carbon fiber. Added features of this grade include: Electrically Conductive.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyvinylidene Fluoride (PVDF)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Carbon fiber filled
Electrically Conductive
High stiffness/Strength

Industry

Material previously used in

Electronic Components
Energy Management
Material Handling

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	202	J/m	ASTM D4812
Izod Impact, notched, 23°C	58	J/m	ASTM D256
Instrumented Dart Impact Energy @ peak, 23°C	11	J	ASTM D3763
Multiaxial Impact	3	J	ISO 6603
*Izod Impact, unnotched 80104 +23°C*	14	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	6	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120 - 150	°C
Drying Time	4	Hrs
Melt Temperature	215 - 230	°C
Front - Zone 3 Temperature	225 - 245	°C
Middle - Zone 2 Temperature	210 - 225	°C
Rear - Zone 1 Temperature	190 - 210	°C
Mold Temperature	65 - 90	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break	78	MPa	ASTM D638
Tensile Strain, break	0.8	%	ASTM D638
Tensile Modulus, 5 mm/min	14270	MPa	ASTM D638
Flexural Stress	127	MPa	ASTM D790
Flexural Modulus	11790	MPa	ASTM D790
Tensile Stress, break	67	MPa	ISO 527
Tensile Strain, break	0.6	%	ISO 527
Tensile Modulus, 1 mm/min	14500	MPa	ISO 527
Flexural Stress	147	MPa	ISO 178
Flexural Modulus	20920	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.769	g/cm³	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.03	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.3 - 0.5	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	1 - 1.3	%	ASTM D955
Mold Shrinkage, flow, 24 hrs	0.36	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	1.16	%	ISO 294
Density	1.76	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.04	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	165	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	159	°C	ASTM D648
CTE, -40°C to 40°C, flow	3.13E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	8.62E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	3.13E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	8.62E-05	1/°C	ISO 11359-2
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	165	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	156	°C	ISO 75/Af

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES