LNP THERMOCOMP 9F005P compound is based on Polycarbonate (PC) resin containing 25% glass fiber. Added features of this grade include: Exceptional Processing, CLTE close to Aluminum.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index | 200 | V | IEC 60112 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥0.75 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 27 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched, 23°C | 449 | J/m | ASTM D4812 |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 33 | kJ/m² | ISO 179/1eU |
| Izod Impact, notched, 23°C | 98 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 7 | J | ASTM D3763 |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 95 - 105 | °C | |
| Drying Time | 2 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 250 - 280 | °C | |
| Nozzle Temperature | 250 - 280 | °C | |
| Front - Zone 3 Temperature | 250 - 280 | °C | |
| Middle - Zone 2 Temperature | 250 - 280 | °C | |
| Rear - Zone 1 Temperature | 250 - 280 | °C | |
| Mold Temperature | 90 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 65 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 130 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 130 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.0 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.0 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 8245 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 166 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7250 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 105 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 105 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 3 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8277 | MPa | ISO 527 |
| Flexural Stress | 168 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7987 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Moisture Absorption (23°C / 50% RH) | .01 | % | ISO 62 |
| Melt Volume Rate, MVR at 260°C/5.0 kg | 47 | cm³/10 min | ISO 1133 |
| Specific Gravity | 1.33 | - | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.06 | % | ASTM D570 |
| Water Absorption, (23°C/saturated) | 0.06 | % | ISO 62-1 |
| Mold Shrinkage, flow, 24 hrs | 0.34 - 0.44 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.53 | % | ISO 294 |
| Mold Shrinkage, flow, 24 hrs | 0.34 - 0.44 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.53 | % | ASTM D955 |
| Melt Flow Rate, 260°C/5.0 kgf | 56 | g/10 min | ASTM D1238 |
| Density | 1.32 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.01 | % | ASTM D570 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 129 | °C | ISO 306 |
| CTE, -40°C to 40°C, flow | 2.68E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 5.67E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 2.68E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, flow | 2.47E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.67E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 6.6E-05 | 1/°C | ISO 11359-2 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 135 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 130 | °C | ASTM D648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 135 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 130 | °C | ISO 75/Af |