LNP™ THERMOCOMP™ Compound 9X22141

LNP THERMOCOMP 9X22141 compound (also known as ER016141) is based on Polycarbonate (PC) and Acrylonitrile butadiene styrene (ABS) resins containing 20% glass fiber. Added features of this grade include: High Stiffness, Excellent Processing, Good Dimensional Stability, Good Impact Performance, UL94 HB Rating

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + ABS (PC+ABS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dimensional stability
Good Processability
High stiffness/Strength
Impact resistant
No PFAS intentionally added

Industry

Material previously used in

Applications

Possible usage of material

Battery Pack
Enclosure/Housing/Cover
battery cover
clamp shell

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥0.75	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	11	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 0°C*	11	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	63	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	12	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	52	kJ/m²	ISO 179/1eU
*Charpy 0°C, V-notch Edgew 80104 sp=62mm*	10	kJ/m²	ISO 179/1eA
Izod Impact, notched, 23°C	110	J/m	ASTM D256
Izod Impact, notched, 0°C	110	J/m	ASTM D256
Izod Impact, unnotched, 23°C	700	J/m	ASTM D4812
Instrumented Dart Impact Energy @ peak, 23°C	18	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80 - 100	°C
Drying Time	2 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	260 - 290	°C
Rear - Zone 1 Temperature	250 - 280	°C
Middle - Zone 2 Temperature	255 - 285	°C
Front - Zone 3 Temperature	260 - 290	°C
Nozzle Temperature	260 - 290	°C
Mold Temperature	60 - 90	°C
Back Pressure	0.2 - 0.7	MPa

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	7000	MPa	ISO 527
Tensile Stress, break, 5 mm/min	114	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.7	%	ISO 527
Flexural Modulus, 2 mm/min	6200	MPa	ISO 178
Flexural Stress, yield, 2 mm/min	166	MPa	ISO 178
Flexural Stress, break, 2 mm/min	165	MPa	ISO 178
Tensile Modulus, 5 mm/min	7000	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	116	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	6600	MPa	ASTM D790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	172	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	169	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.29	g/cm³	ISO 1183
Melt Flow Rate, 260°C/2.16 kgf	5	g/10 min	ASTM D1238
Melt Flow Rate, 260°C/5.0 kgf	20	g/10 min	ASTM D1238
Mold Shrinkage, flow	0.2 - 0.4	%	SABIC method
Mold Shrinkage, xflow	0.3 - 0.5	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Relative Temp Index, Elec	60	°C	UL 746B
Relative Temp Index, Mech w/impact	60	°C	UL 746B
Relative Temp Index, Mech w/o impact	60	°C	UL 746B
Vicat Softening Temp, Rate B/50	136	°C	ISO 306
Vicat Softening Temp, Rate B/120	138	°C	ISO 306
CTE, -30°C to 80°C, flow	3.8E-5	1/°C	ISO 11359-2
CTE, -30°C to 80°C, xflow	5.8E-5	1/°C	ISO 11359-2
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	132	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	137	°C	ISO 75/Bf
HDT, 1.82 MPa, 3.2mm, unannealed	132	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	136	°C	ASTM D648

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES