LNP THERMOCOMP AF006 compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 30% glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 - 0.1 | % | |
| Melt Temperature | 260 | °C | |
| Front - Zone 3 Temperature | 265 - 275 | °C | |
| Middle - Zone 2 Temperature | 230 - 245 | °C | |
| Rear - Zone 1 Temperature | 205 - 215 | °C | |
| Mold Temperature | 70 - 80 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 82 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7900 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 103 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6300 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow | 0.12 | % | SABIC method |
| Density | 1.26 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 2.3E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 6.5E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 104 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 98 | °C | ISO 75/Af |