LNP™ THERMOCOMP™ Compound AX02749

LNP THERMOCOMP AX02749 compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 20% glass fiber.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Acrylonitrile Butadiene Styrene (ABS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
No PFAS intentionally added

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Monitoring and Imaging

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	7	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	23	kJ/m²	ISO 180/1U
Multiaxial Impact	2	J	ISO 6603
Izod Impact, notched, 23°C	80	J/m	ASTM D256
Izod Impact, unnotched, 23°C	374	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	13	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.05 - 0.1	%
Melt Temperature	260	°C
Front - Zone 3 Temperature	265 - 275	°C
Middle - Zone 2 Temperature	230 - 245	°C
Rear - Zone 1 Temperature	205 - 215	°C
Mold Temperature	70 - 80	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	77	MPa	ISO 527
Tensile Strain, break, 5 mm/min	1.8	%	ISO 527
Tensile Modulus, 1 mm/min	6040	MPa	ISO 527
Flexural Stress	119	MPa	ISO 178
Flexural Modulus, 2 mm/min	5970	MPa	ISO 178
Tensile Stress, brk, Type I, 5 mm/min	76	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2	%	ASTM D638
Tensile Modulus, 50 mm/min	6080	MPa	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	122	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	6080	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.19	g/cm³	ISO 1183
Mold Shrinkage, flow, 24 hrs	0.2 - 0.5	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.4 - 0.7	%	ISO 294
Specific Gravity	1.19	-	ASTM D792
Moisture Absorption, (23°C/50% RH/24 hrs)	0.25	%	ASTM D570
Mold Shrinkage, flow, 24 hrs	0.2 - 0.5	%	ASTM D955
Mold Shrinkage, xflow, 24 hrs	0.4 - 0.7	%	ASTM D955

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	100	°C	ISO 75/Af
HDT, 1.82 MPa, 3.2mm, unannealed	100	°C	ASTM D648
CTE, -30°C to 30°C, flow	5.20E-05	1/°C	ASTM D696
CTE, -30°C to 30°C, xflow	5.60E-05	1/°C	ASTM D696

Register for High value Multi-Point Data